Quenching steel results in transformation of austenite into martensite, it is not completely transformed. There are some of the crystals of austenite that remain unchanged and are not affected by quenching below martensite-finish temperature. This can further be transformed into martensite, through slow cooling of the metal at extremely lower temperatures. Normally, cold treating includes […]